Description：With PLA, PBAT and other fully biodegradable materials as the main raw materials, we have developed several series of fully biodegradable modified resins for different application scenarios. According to the different processing methods, they can be divided into special materials for film bags, extrusion materials, and special materials for blister molding. The modified resins comply with GB/T, EN, ASTM and other fully biodegradable standards, and some of the materials meet the food contact requirements. We have been registered with FDA in the U.S.A. We strive to bring healthy and environmentally friendly fully biodegradable materials to our customers at home and abroad.
Category：Flame retardant, stiffener
Characteristic：High oxygen index, high impact resistance
Application：Bumpers, grilles, centre consoles, bus panels, low-voltage electrical switches, new energy charging system parts, battery housings, power drive housings, etc.
Details about CA-9100-LV
High oxygen index extrusion grade modified PC/ABS
|Characteristics and application fields|
High oxygen index, high impact resistance, suitable for automotive interior panels, building materials and other fields.
|test item test condition testing nominative||unit||reference value|
|Basic physical properties|
|proportion 23℃ ISO 1183||g/cm3||1.16|
|melt flow rate 260℃，5KG ISO 1133||g/10min||25|
|tensile-strength 50mm/min ISO 527-2||MPa||60|
|elongation at break 50mm/min ISO 527-2||%||30|
|flexural strength 2mm/min ISO 178||MPa||85|
|flexural modulus 2mm/min ISO 178||MPa||2300|
|Notch impact strength of simply supported beam 23℃ ISO 179-1||KJ/㎡||45|
|distortion temperature 0.45MPa ISO 75-2||℃||100|
|Vicat softening temperature temperature B50 ISO 306||℃||100|
|oxygen index GB 2406.2||%||＞25|
|Suggested processing conditions|
|Injection molding temperature||℃||220-250|