PA Modified Engineering Plastics EN-2000-KL NC001
Description：With PLA, PBAT and other fully biodegradable materials as the main raw materials, we have developed several series of fully biodegradable modified resins for different application scenarios. According to the different processing methods, they can be divided into special materials for film bags, extrusion materials, and special materials for blister molding. The modified resins comply with GB/T, EN, ASTM and other fully biodegradable standards, and some of the materials meet the food contact requirements. We have been registered with FDA in the U.S.A. We strive to bring healthy and environmentally friendly fully biodegradable materials to our customers at home and abroad.
Category：PA66: high wear resistance, self-lubricating, high rigidity
Brand：EN-2000-KL NC001
Characteristic：Resistant to low temperature -40℃, strong toughness
Application：Automotive industry, instrument housings, nylon cable ties and other products requiring high impact resistance and high strength
Details about PA Modified Engineering Plastics EN-2000-KL NC001
product description Low-temperature-resistant, Toughened Injection-grade Modified PA66 application area High toughness and low temperature resistance -40℃. Suitable for automobile field, sporting goods, cable tie and other supplies.
Typical performance
| test item | test condition | testing nominative | unit | reference value |
| Basic physical properties | ||||
| melt flow rate | 275℃，5kg | ISO 1133 | g/10min | 29.14 |
| proportion | 23±2℃ | ISO 1183 | g/cm3 | 1.08 |
| mechanical character | ||||
| tensile-strength | 50mm/min | ISO 37 | MPa | 54 |
| elongation at break | 50mm/min | ISO 37 | % | 55 |
| flexural strength | 2mm/min | ISO 178 | MPa | 70.2 |
| flexural modulus | 2mm/min | ISO 178 | MPa | 1713 |
| Notched impact strength of cantilever beam | 5.5J | ISO 179-1 | KJ/m2 | 62 |
| hot property | ||||
| distortion temperature | 1.8MPa | ISO 75-2 | ℃ | 54.7 |
| melting point | 23±2℃ | ISO 11357-3 | ℃ | 258 |
| flame retardation | ||||
| fire resistance | 1.6mm | UL94 | Class | HB |
| Glowing filament combustion index | / | IEC 60695 | S/ | |
| electrical property | ||||
| comparative tracking index | 23±2℃ | IEC60112 | V | 500 |
| Suggested processing conditions | ||||
| drying temperature | ℃ | 100-140 | ||
| drying time | h | 3-4 | ||
| Injection molding temperature | ℃ | 265-275 | ||
| Injection pressure | MPa | 75-85 | ||